UHP 550mm Graphite Electrode
Graphitization bụ ọkwa dị oke mkpa na mmepụta electrode graphite UHP.Ọ na-ezo aka na usoro ọgwụgwọ okpomọkụ dị elu nke ngwaahịa carbon n'elu 2300 ℃ n'ime ọkụ ọkụ eletrik na-ekpo ọkụ iji tọghata carbon chaotic oyi akwa amorphous ka ọ bụrụ usoro kristal graphite nyere iwu akụkụ atọ.
Gịnị bụ ọrụ nke graphitization?
* Melite ọkụ eletrik na ọkụ ọkụ
* Melite nguzogide ujo na nkwụsi ike kemịkalụ (ọnụahịa mgbasawanye ahịrị na-ebelata site na 50-80%);
* Mee ka ihe carbon nwee mmanu ma na-eyi nguzogide;
* Na-ewepụ ihe ndị na-adịghị ọcha ma melite ịdị ọcha nke ihe carbon (ọdịnaya ntụ nke ngwaahịa na-ebelata site na 0.5% ruo ihe dịka 0.3%).
| Nkọwa nka na ụzụ atụnyere maka UHP Graphite Electrode 22" | ||
| Electrode | ||
| Ihe | Nkeji | Specific Supplier |
| Ụdị njirimara osisi | ||
| Ọnụ ala dayameta | mm | 550 |
| Oke dayameta | mm | 562 |
| Obere dayameta | mm | 556 |
| Ogologo aha aha | mm | 1800-2400 |
| Ogologo Ogologo | mm | 1900-2500 |
| Ogologo Min | mm | 1700-2300 |
| Njupụta nnukwu | g/cm3 | 1.68-1.72 |
| transverse ike | MPa | ≥12.0 |
| Modul na-eto eto | GPA | ≤13.0 |
| Nguzogide akọwapụtara | µΩm | 4.5-5.6 |
| Oke njupụta ugbu a | KA/cm2 | 18-27 |
| Ike ibu ugbu a | A | 45000-65000 |
| (CTE) | 10-6 ℃ | ≤1.2 |
| ntụ ọdịnaya | % | ≤0.2 |
| Ụdị njirimara nke ara ara (4TPI) | ||
| Njupụta nnukwu | g/cm3 | 1.78-1.84 |
| transverse ike | MPa | ≥22.0 |
| Modul na-eto eto | GPA | ≤18.0 |
| Nguzogide akọwapụtara | µΩm | 3.4-3.8 |
| (CTE) | 10-6 ℃ | ≤1.0 |
| ntụ ọdịnaya | % | ≤0.2 |